Failure state: O ring appears obvious curl
Failure reason: the installation causes, the movement speed is too low, the material is too hard or the elasticity is too small, the O ring surface treatment is uneven, the groove size is uneven, the groove surface is rough, the lubrication is insufficient.
Solution: proper installation, use of high elastic material, appropriate to improve the design and surface smoothness of the groove, as far as possible to use the support ring.
(3) Over compression
Failure state: O ring, the contact surface is flat deformation, and may be accompanied by cracks.
Failure reason: the design is unreasonable, without considering the material due to heat and chemical medium caused by deformation, or too much pressure caused by deformation.
Solution: the design of the trench shall take into account the deformation of the material due to temperature and chemical medium.
(4) Permanent compression deformation
Failure state: the contact surface of the seal presents a flat permanent deformation.
Failure reason: too much pressure; too high temperature; the material has not completed curing; the material itself has a permanent deformation rate; the material is too expansive in the chemical medium.
Solution: choose low deformation material; proper groove design; confirm material compatibility with medium.
(5) Chemical corrosion damage
Failure state: chemical corrosion can cause various defects in the O ring, such as foaming, cracking, small holes, or fading. At some point, chemical corrosion can only be obtained by measuring its physical properties by means of an instrument.
Failure cause: material not in accordance with medium or excessive temperature.
Solution: choose more resistant chemical medium corrosion of the material.
Failure state: O type ring, all or part of the sealing area, wear and tear, can be found in the sealing surface of materials wear particles.
Failure reasons: sealing surface finish is not enough, the temperature is too high, the sealing environment into the wear debris, sealing parts produce relative movement, sealing surface treatment is not complete.
Solution: improve groove finish, choose self lubrication material, and clearly cause worn parts and environment.
The state of failure: O ring appears on the surface of bubbles, pits, scars; a lot of pressure when the material absorption gas, when the pressure suddenly decreases, the gas absorption materials caused by the O ring run fast, surface blasting.
Failure reason: pressure changes too fast, material hardness and elasticity are too low.
Solution: choose higher hardness, better elasticity of material, reduce the speed of decompression.
(8) Debris pollution
Failure state: O ring section of foreign body.
Failure reason: the production process is polluted by the environment, and the material is corroded or reacted. The material is non - semiconductor grade material.
Solution: indicate cleanliness of production and packaging requirements, and strengthen environmental control during production and transportation of O rings.
(9) Hot corrosion
Failure state: the high temperature contact surfaces of O rings exhibit radial cracks, and some may soften or become more lustrous due to excessive temperature.
Failure reason: the material can not withstand high temperature or temperature beyond the design temperature, or the temperature changes too frequently.
Solution: choose materials with high temperature resistance, such as possible to reduce the sealing surface temperature.